G10 Insulating Glass Epoxy Laminate
Mafiafia masani: 0.5~100mm
Tele masani: 1020×2040mm
Fa'aeletoroni vasega alkali-saoloto ie tioata tioata ua impregnated i faaulufale mai resin epoxy, ma faaopoopo i le tali afi faaulufaleina tutusa retardants, pipii ma isi additives, ma faagaoioia e omi vevela.Fa'asa'o le afi vasega UL94-VO vasega, mea fa'ainisinia lelei i le maualuga o le vevela, lelei le fa'atinoina o galuega ma le fa'aogaina o le fa'aogaina.
G10 epoxy laupapa talosaga: faʻaaogaina e pei o le faʻapipiʻiina o vaega faʻavae i totonu o afi ma mea eletise, e pei o vaʻavaʻavaʻa, sui kapoti, transformers, afi DC, faʻafesoʻotaʻi AC, mea faʻapipiʻi eletise ma isi mea eletise.
Leai. | Aitema | Vaega | Tulaga Taua | I'uga o su'ega |
1 | Malosi fa'afoliga fa'asagatonu i laminations | MPa | GB/T1303.4-2009 | ≥340 |
2 | Pi'o fa'apipi'i fa'apipi'i | MPa | GB/T1303.4-2009 | / |
3 | Notch A'afiaga malosi tutusa ma lamination (charpy) | kJ/m2 | GB/T1303.4-2009 | ≥33 |
4 | Malosi fa'asa | MPa | GB/T1303.4-2009 | / |
5 | Malosi dielectric perpendicular to laminations (i le suauu 20±2℃) | KV/mm | GB/T1303.4-2009 | ≥11.4 |
6 | Malosiaga malepelepetutusa ma lamination (i le suauu90±2℃) | KV | GB/T1303.4-2009 | ≥35 |
7 | 1 MHz mea leiloa | / | GB/T1303.4-2009 | / |
8 | Fa'agata fa'a'ese'ese fa'asusu i le vai | MΩ | GB/T1303.4-2009 | ≥5x10000 |
9 | CTI | / | GB/T 4207-2012 | / |
10 | Suavai | mg | GB/T 1303.4-2009 | ≤27 |
11 | Malosi | g/cm3 | GB/T 1303.4-2009 | / |